Atomically dispersed Ni is coke-resistant for dry reforming of methane

Increase font size  Decrease font size Date:2019-11-18   Views:349

Dry reforming of methane (DRM) is the process of converting methane (CH4) and carbon dioxide (CO2) into synthesis gas (syngas). Since CO2 and CH4 are the two most important atmospheric greenhouse gases (GHGs), as well as abundant and low-cost carbon sources, DRM has the potential to mitigate rising GHG emissions and simultaneously realize clean(er) fossil fuel utilization.

Ni catalysts are the most promising candidates for DRM due to their low cost and high initial activity. However, in situ catalyst deactivation caused mainly by carbon deposition (coking) has hindered their commercial use.

Scientists at the Dalian Institute of Chemical Physics (DICP) of the Chinese Academy of Sciences have now developed a completely coke-resistant Ni-based single-atom catalyst (SAC). Their findings were published in Nature Communications.

The researchers first developed a hydroxyapatite-(HAP) supported Ni SAC, studied its DRM performance, and found that both HAP-supported Ni SAC and Ni nanocatalyst deactivated quickly during high-temperature DRM.

However, characterization of the samples used revealed that the deactivation mechanisms were totally different: Deactivation of the nanocatalyst originated with the coke, while deactivation of Ni SAC stemmed from the sintering of Ni single atoms without any coke formation. These results implied that highly stable and coke-resistant Ni SAC could be obtained if Ni single atoms were effectively stabilized upon reaction.

The scientists then doped HAP with cerium to stabilize Ni single atoms through strong metal-support interaction. The resulting HAP-Ce-supported Ni SAC was highly stable upon reaction, without any coke formation.

Further studies revealed that Ni SAC is intrinsically coke-resistant. In other words, no coke was formed at all during the reaction (in contrast with coke being formed then removed). The coke resistance of Ni SAC derives from the catalyst's unique capacity for selective activation of the first C-H bond in CH4.

 
 
[ Search ]  [ ]  [ Email ]  [ Print ]  [ Close ]  [ Top ]

 
Total:0comment(s) [View All]  Related comment

 
Recomment
Popular
 
 
Home | About | Service | copyright | agreement | contact | about | SiteMap | Links | GuestBook | Ads service | 京ICP 68975478-1
Tel:+86-10-68645975           Fax:+86-10-68645973
E-mail:yaoshang68@163.com     QQ:1483838028